A new series of [n]-oligoureas ([n]-OUs, n=4, 7, 10, and 12) green solid sorbents was prepared following a base-catalyzed, microwave-assisted oligomerization reaction. The materials were characterized by NMR and IR spectroscopy, elemental analysis, thermogravimetric analysis, differential scanning calorimetry, and XRD. Decomposition temperatures at 50 % weight loss (Td50 ) were ca. 350 °C for all oligomers. Urea and urethane functional groups indicated by IR spectroscopy confirmed the formation of the sorbent. The CO2 capturing capacities were determined at 35 °C and 1.0 bar (gravimetric method). Accordingly, [10]-OU had the highest CO2 sorption capacity among the others (18.90 and 22.70 mg CO 2 gsorbent (-1) ) at two different activation temperatures (60 or 100 °C, respectively). Chemisorption was the principal mechanism for CO2 capture. Cyclic CO2 sorption/desorption measurements were carried out to test the recyclability of [10]-OU. Activating the sample at 60 °C, three stable CO2 sorption cycles were achieved after running the first cycle. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim. https://www.researchgate.net/publication/275245666_n-Oligourea-Based_Green_Sorbents_with_Enhanced_CO2_Sorption_Capacity
A new series of [n]-oligoureas ([n]-OUs, n=4, 7, 10, and 12) green solid sorbents was prepared following a base-catalyzed, microwave-assisted oligomerization reaction. The materials were characterized by NMR and IR spectroscopy, elemental analysis, thermogravimetric analysis, differential scanning calorimetry, and XRD. Decomposition temperatures at 50 % weight loss (Td50 ) were ca. 350 °C for all oligomers. Urea and urethane functional groups indicated by IR spectroscopy confirmed the formation of the sorbent. The CO2 capturing capacities were determined at 35 °C and 1.0 bar (gravimetric method). Accordingly, [10]-OU had the highest CO2 sorption capacity among the others (18.90 and 22.70 mg CO 2 gsorbent (-1) ) at two different activation temperatures (60 or 100 °C, respectively). Chemisorption was the principal mechanism for CO2 capture. Cyclic CO2 sorption/desorption measurements were carried out to test the recyclability of [10]-OU. Activating the sample at 60 °C, three stable CO2 sorption cycles were achieved after running the first cycle. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
https://www.researchgate.net/publication/275245666_n-Oligourea-Based_Green_Sorbents_with_Enhanced_CO2_Sorption_Capacity
17.Apr.2024
16.Jan.2024
20.Sep.2023
أنا طالبة في الهندسة الصناعية, اختياري لهذا التخصص كان بناءً على أهميته الكبيرة كمهنة في الحاضر والمستقبل ... رغد بركات
الهندسة الصناعية تساعدك على اتخاذ قرارات أفضل، وتعطي أشكالا أخرى من مبادئ الهندسة بشكل عملي وعلمي في آن. ... محمود صلاح
قسم الهندسة الكيميائية قسم جميل جدا تعلمت فيه الكثير ومما تعلمته فيه جدية العمل وروح الفريق الواحد .. ... رغد الشويكي